Alumiiniumi jootmine / keevitus
MargoU - 16.04.09 10:38

Kas keegi on katsetanud jootmist nagu näha videol http://www.durafixbaltic.eu/


DonNiger - 16.04.09 15:25

Olen neid videosi näinud aga pulkade leidmisega raskusi.
Alumiiniumi on tavaliselt üsna kehv keevitada.


rocket - 16.04.09 15:52

Mul on ka olemas üks joodise varras, mis sobib alumiiniumile, aga see nõuab lisaks ka pastat !!!


MargoU - 16.04.09 16:33

http://www.durafixbaltic.eu/ nagu mina aru saan siis selle lehe kaudu peaks saama osta.


samru - 16.04.09 18:25

Tsitaat:
Algselt postitas: MargoU
http://www.durafixbaltic.eu/ nagu mina aru saan siis selle lehe kaudu peaks saama osta.


Nagu mina aru saan oled sa päris mitmes foorumis seda linki jaganud :P, juu siis ise tegeled sellega. Seleta inimestele millega tegu, keevitamisega igaljuhul mitte.


MargoU - 16.04.09 19:51

Ei tegele ise.
Nimelt ühel sõbral msnis oli see lehekülg pealkirjaks.
Vaatasin ja tundus päris huvitav. Youtubes neid videosid rohkem. Taastavad keermeid jne.
Uurisin ka sellelt sõbralt et kas päriselt on ka nii lihtne ja kas ta on katsetanud. Kahjuks vastust ei saanud hetkel, kuid lähipäevadel saan temaga kokku ja võtan kindlasti teema üles.
Teema püstitasin tõesti mõnesse foorumisse, kuna neti.ee otsing ei andnud mingeid tulemusi.


olbert - 16.04.09 19:54

Tsitaat:
Algselt postitas: DonNiger
Alumiiniumi on tavaliselt üsna kehv keevitada.


Mis tähendab, et "tavaliselt üsna kehv keevitada"? Kui ikka ei oska keevitada siis vast on ikka jah üsna kehv keevitada!

Ei tea, kas ma uväide nüüd paika ka peab aga kaldun arvama, et see on tavaline TIG-i traat.


Rain573 - 16.04.09 20:04

Sellega peaks saama siis küünlaaugu keeret ka taastada? Kui mõni seda teeks oleks kül ülikõva! Oleks kohe käpp. Pronkspuks tundub kuidagi kahtlane. Üks küünal jääb teistest kõrgemale jne...:(


wookie - 16.04.09 20:07

http://www.hotrodders.com/forum/durafix-48439.html
Tensile strength is usually measured by taking a test bar and pulling on it in a machine until it breaks. The thing they are not telling you is how thick of a test bar was it. I have done this at work many times for aerospace. You can pull a 1/4" test bar and a 1/2" test bar and vary the tensile results greatly. These ratings are usually done under perfect conditions with perfect alloy. How thick is your weld and how perfect (no impurity and so on). A typical grade 8 bolt is rated to 96000 lbs, but I would not trust my life by hanging that much weight on a 1/4" bolt of any kind.

As a measure of safety, engineers usually specify a 10 to 1 ratio for safety reasons. I have never , ever found a chemical adhesion such as braze to be comparable in strength as a weld that uses parent metal and mechanical dispersion to join metals. In other words, MIG it, TIG it or Gas weld with penetration, no chemical flow type brazing for ultimate strength. For cosmetics, yup, works great.


Seega, see keemia ilmselt ei asenda keevitust.


mkb - 19.04.09 08:30

Tsitaat:
Algselt postitas: Rain573
Sellega peaks saama siis küünlaaugu keeret ka taastada? Kui mõni seda teeks oleks kül ülikõva! Oleks kohe käpp. Pronkspuks tundub kuidagi kahtlane. Üks küünal jääb teistest kõrgemale jne...:(

Tsiteerin E21.ee foorumist kasutaja Karu juttu, ehk on abiks.
--------------------------------------------------------------------------------

meile tuleb see lätist, uurin hinna välja siis näeb palju hinna vahe on ülaldoodud lingiga joodame sellega radikaid,erinevaid kartereid kus ei toihi pinnad ära tommata(tavaline tig kisub kõveraks kõik) saab taastatada erinevaid keerme auke, puurid vana keerme välja ja sulatad joodise sisse ja siis uus auk ja keere.